| Alloy | Type | Current type | Current (A) | Voltage (V) | Wire feed speed (m/min) | Welding speed (mm/s) | Shielding gas | Gas flow rate (l/min) | Weld joint | Spatter formation | Cleaning action | Process |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| 4043 | AlSi5 | AC | 110 | 18,4 | 5 | 14 | Ar 100% | 12 | very good | none | very good | Pulse |
| 4043 | AlSi5 | AC | 103 | 18,5 | 5,5&4 | 11 | Ar 100% | 12 | very good | none | very good | DPulse |
| 4047 | AlSi12 | AC | 104 | 18,5 | 5 | 14,5 | Ar 100% | 12 | very good | none | very good | Pulse |
| 4047 | AlSi12 | AC | 98 | 18,3 | 5,5&4 | 12,5 | Ar 100% | 12 | very good | none | very good | DPulse |
| 5087 | AlMg4,5MnZr | AC | 139 | 18,4 | 8 | 14 | Ar 100% | 12 | very good | none | very good | Pulse |
| 5087 | AlMg4,5MnZr | AC | 134 | 18,2 | 9&7 | 12,5 | Ar 100% | 12 | very good | none | very good | DPulse |
| 5183 | AlMg4,5Mn0,7 | AC | 136 | 18,3 | 8 | 14 | Ar 100% | 12 | good | few | good | Pulse |
| 5183 | AlMg4,5Mn0,7 | AC | 132 | 18,4 | 9&7 | 12,5 | Ar 100% | 12 | very good | none | very good | DPulse |
| 5356 | AlMg5Cr | AC | 138 | 18,7 | 8 | 14 | Ar 100% | 12 | very good | none | good | Pulse |
| 5356 | AlMg5Cr | AC | 130 | 17,7 | 9&7 | 12,5 | Ar 100% | 12 | good | none | good | DPulse |
| 5554 | AlMg2,7 | AC | 147 | 18,6 | 8 | 14 | Ar 100% | 12 | good | few | good | Pulse |
| 5554 | AlMg2,7 | AC | 136 | 18,1 | 9&7 | 12,5 | Ar 100% | 12 | good | few | good | DPulse |
| 5754 | AlMg3 | AC | 146 | 18 | 8 | 14 | Ar 100% | 12 | very good | none | good | Pulse |
| 5754 | AlMg3 | AC | 135 | 18,8 | 9&7 | 11 | Ar 100% | 12 | very good | none | very good | DPulse |